Thickness | EN 438-2 section 5 | According to the required thickness | 02.0 < t < 03.0 mm: ± 0.20mm 03.0 < t < 05.0 mm: ±0.30mm 05.0 < t < 08.0 mm: ±0.40mm 08.0 < t < 12.0 mm: ±0.50mm 12.0 < t < 16.0 mm: ±0.60mm 16.0 < t < 20.0 mm: ±0.70mm 20.0 < t < 25.0 mm: ±0.80mm |
Density | ISO 1183-1 | 1.4 | Min. 1.35GR/CM3 |
Wear Resistance | EN 438-2 section 10 CGS | IP=185 Rev. Wear Value=485 Rev. | Initial Point> 150 Rev. Wear Value > 350Rev. |
Scratch Resistance | EN 438-2 section 25 CGS | 3N 4N |
Flat Surface Min. 2N, Textured Surface Min. 3N |
Impact Resistance | EN 438-2 Big Ball section 21CGS 2.0 <t< 6.0mm t>6.0mm | No Crack, 4.5 mm No Crack, 3.5 mm | 1400 mm height: no crack.50mm Max. 1800 mm height: no crack, 50mm Max. |
Resistance to Crazing (20 Hours @80◦c) |
EN 438-2 section 24 CGS | Level 4 | Min. level 4 |
Resistance to Dry Heatatat180◦c | EN 438-2 section 16 CGS Glossy Surface Finish Other Surface Finish |
Level 4 Level 5 |
Min. Level 3 Min. Level 4 |
Resistance to Water Vapor | EN 438-2 section 14 CGS Glossy Surface Finish Other Surface Finish |
Level 4 Level 5 |
Min. Level 3 Min. Level 4 |
Resistance to Boiling Water | EN 438-2 section 12 CGS2<t<5.0mm i>5.0mm Glossy Surface Finish Other surface Finish |
2.2% 3.1% 0.55% 0.65% Level 4 Level 5 |
Max. 5% in Weight Max. 6% in thickness Max. 2% in weight Max. 2% in thickness Min. Levels Min. Level 4 |
Resistance to Cigarette Burn | EN 438-2 section 30 CGS | Level 4 | Min. Levels |
Resistance to Staining | EN 438-2 Section 26 CGS Group 1+2 Group 3 |
Level 5 Level 5 |
Min. Levels Min. Level 4 |
Flatness | EN 438-2 Section 9 CGS 2.0<t<6.0mm 6.0<t< 10.0mm t> 10.0 mm |
1.23mm |
Max. 8 mm / 1 M Length |
Light fastness | EN 438-2 Section 27 CGS Grey Scale |
Level 5 | Min. level 4 |
High Temp, stability 70◦c | EN 438-2 Section 17 CGS 2.0<t<5.0mm t> 5.0mm |
Level: 0.22 mm W: 0.35mm L: 0.18mm W: 0.23mm |
L: Max. 0.4 mm W: Max. 0.8 mm L: Max. 0.3 mm W: Max. 0.6 mm |
Tensile Strength | EN ISO 527-2CGS | 35 Mpa | Min.60Mpa |
Flexural Strength | EN ISO 178 EDS, EOF | 114 Mpa | Min.80Mpa |
Flexural Modulus | EN ISO 178 EDS, EOF | 16. 522 Mpa | Min.9000Mpa |
Coefficient of Linear Thermal expansion(COTE) |
ASTM D696-08 | 6. OX 10 | Rnm~/mrrrc |